AWS ER80S-D2 vs. C55281 Copper

AWS ER80S-D2 belongs to the iron alloys classification, while C55281 copper belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-D2 and the bottom bar is C55281 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
40
Tensile Strength: Ultimate (UTS), MPa 620
190

Thermal Properties

Latent Heat of Fusion, J/g 260
190
Melting Completion (Liquidus), °C 1450
810
Melting Onset (Solidus), °C 1410
640
Specific Heat Capacity, J/kg-K 470
400
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.7
Embodied Carbon, kg CO2/kg material 1.6
7.0
Embodied Energy, MJ/kg 21
110

Common Calculations

Stiffness to Weight: Axial, points 13
6.9
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 22
6.1
Strength to Weight: Bending, points 21
8.5
Thermal Shock Resistance, points 18
7.7

Alloy Composition

Carbon (C), % 0.070 to 0.12
0
Copper (Cu), % 0 to 0.5
88.5 to 89.4
Iron (Fe), % 95.2 to 97.4
0
Manganese (Mn), % 1.6 to 2.1
0
Molybdenum (Mo), % 0.4 to 0.6
0
Nickel (Ni), % 0 to 0.15
0
Phosphorus (P), % 0 to 0.025
5.8 to 6.2
Silicon (Si), % 0.5 to 0.8
0
Silver (Ag), % 0
4.8 to 5.2
Sulfur (S), % 0 to 0.025
0
Residuals, % 0
0 to 0.15