AWS ER80S-Ni2 vs. EN 1.0454 Cast Steel

Both AWS ER80S-Ni2 and EN 1.0454 cast steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-Ni2 and the bottom bar is EN 1.0454 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
25
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 620
550
Tensile Strength: Yield (Proof), MPa 540
300

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1410
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 3.4
1.7
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 22
18
Embodied Water, L/kg 51
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
110
Resilience: Unit (Modulus of Resilience), kJ/m3 770
240
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
19
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 18
17

Alloy Composition

Carbon (C), % 0 to 0.12
0
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 94.2 to 97.6
99.935 to 100
Manganese (Mn), % 0 to 1.3
0
Nickel (Ni), % 2.0 to 2.8
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0.4 to 0.8
0
Sulfur (S), % 0 to 0.025
0 to 0.030
Residuals, % 0 to 0.5
0