AWS ER80S-Ni2 vs. EN 1.4021 Stainless Steel
Both AWS ER80S-Ni2 and EN 1.4021 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AWS ER80S-Ni2 and the bottom bar is EN 1.4021 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 27 | |
| 11 to 17 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 630 to 880 |
| Tensile Strength: Yield (Proof), MPa | 540 | |
| 390 to 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 270 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1440 |
| Melting Onset (Solidus), °C | 1410 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 52 | |
| 30 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.4 | |
| 7.0 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 1.9 |
| Embodied Energy, MJ/kg | 22 | |
| 27 |
| Embodied Water, L/kg | 51 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 | |
| 88 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 770 | |
| 400 to 1160 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 22 | |
| 23 to 31 |
| Strength to Weight: Bending, points | 21 | |
| 21 to 26 |
| Thermal Diffusivity, mm2/s | 14 | |
| 8.1 |
| Thermal Shock Resistance, points | 18 | |
| 22 to 31 |
Alloy Composition
| Carbon (C), % | 0 to 0.12 | |
| 0.16 to 0.25 |
| Chromium (Cr), % | 0 | |
| 12 to 14 |
| Copper (Cu), % | 0 to 0.35 | |
| 0 |
| Iron (Fe), % | 94.2 to 97.6 | |
| 83.2 to 87.8 |
| Manganese (Mn), % | 0 to 1.3 | |
| 0 to 1.5 |
| Nickel (Ni), % | 2.0 to 2.8 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.4 to 0.8 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |
| Residuals, % | 0 to 0.5 | |
| 0 |