AWS ER80S-Ni3 vs. R30155 Cobalt
Both AWS ER80S-Ni3 and R30155 cobalt are iron alloys. They have a modest 35% of their average alloy composition in common, which, by itself, doesn't mean much. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS ER80S-Ni3 and the bottom bar is R30155 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 27 | |
| 34 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 850 |
| Tensile Strength: Yield (Proof), MPa | 530 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 300 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1470 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 51 | |
| 12 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.0 | |
| 80 |
| Density, g/cm3 | 7.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 9.7 |
| Embodied Energy, MJ/kg | 23 | |
| 150 |
| Embodied Water, L/kg | 52 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 | |
| 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 740 | |
| 370 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 22 | |
| 28 |
| Strength to Weight: Bending, points | 21 | |
| 24 |
| Thermal Diffusivity, mm2/s | 14 | |
| 3.2 |
| Thermal Shock Resistance, points | 19 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.12 | |
| 0.080 to 0.16 |
| Chromium (Cr), % | 0 | |
| 20 to 22.5 |
| Cobalt (Co), % | 0 | |
| 18.5 to 21 |
| Copper (Cu), % | 0 to 0.35 | |
| 0 |
| Iron (Fe), % | 93.2 to 96.6 | |
| 24.3 to 36.2 |
| Manganese (Mn), % | 0 to 1.3 | |
| 1.0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 3.0 to 3.8 | |
| 19 to 21 |
| Niobium (Nb), % | 0 | |
| 0.75 to 1.3 |
| Nitrogen (N), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.4 to 0.8 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0 | |
| 0.75 to 1.3 |
| Tungsten (W), % | 0 | |
| 2.0 to 3.0 |
| Residuals, % | 0 to 0.5 | |
| 0 |