AWS ER90S-B3 vs. EN 1.0558 Cast Steel

Both AWS ER90S-B3 and EN 1.0558 cast steel are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS ER90S-B3 and the bottom bar is EN 1.0558 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
18
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 690
640
Tensile Strength: Yield (Proof), MPa 620
340

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
1.7
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 24
18
Embodied Water, L/kg 60
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
99
Resilience: Unit (Modulus of Resilience), kJ/m3 1000
300
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
22
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 20
20

Alloy Composition

Carbon (C), % 0.070 to 0.12
0
Chromium (Cr), % 2.3 to 2.7
0
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 93.5 to 95.9
99.935 to 100
Manganese (Mn), % 0.4 to 0.7
0
Molybdenum (Mo), % 0.9 to 1.2
0
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0.4 to 0.7
0
Sulfur (S), % 0 to 0.025
0 to 0.030
Residuals, % 0 to 0.5
0