AWS ER90S-B9 vs. EN 1.0625 Steel

Both AWS ER90S-B9 and EN 1.0625 steel are iron alloys. They have 89% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS ER90S-B9 and the bottom bar is EN 1.0625 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
25
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 690
560
Tensile Strength: Yield (Proof), MPa 470
320

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 25
47
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
2.2
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.5
Embodied Energy, MJ/kg 37
20
Embodied Water, L/kg 91
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 570
270
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25
20
Strength to Weight: Bending, points 22
19
Thermal Diffusivity, mm2/s 6.9
13
Thermal Shock Resistance, points 19
18

Alloy Composition

Aluminum (Al), % 0 to 0.040
0
Carbon (C), % 0.070 to 0.13
0.18 to 0.25
Chromium (Cr), % 8.0 to 10.5
0 to 0.3
Copper (Cu), % 0 to 0.2
0 to 0.3
Iron (Fe), % 84.4 to 90.7
96.6 to 99.02
Manganese (Mn), % 0 to 1.2
0.8 to 1.4
Molybdenum (Mo), % 0.85 to 1.2
0 to 0.12
Nickel (Ni), % 0 to 0.8
0 to 0.4
Niobium (Nb), % 0.020 to 0.1
0
Nitrogen (N), % 0.030 to 0.070
0
Phosphorus (P), % 0 to 0.010
0 to 0.030
Silicon (Si), % 0.15 to 0.5
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.020
Vanadium (V), % 0.15 to 0.3
0 to 0.030
Residuals, % 0 to 0.5
0