AWS ER90S-D2 vs. EN 1.4122 Stainless Steel
Both AWS ER90S-D2 and EN 1.4122 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AWS ER90S-D2 and the bottom bar is EN 1.4122 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 19 | |
| 14 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 790 to 850 |
| Tensile Strength: Yield (Proof), MPa | 600 | |
| 450 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 280 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1440 |
| Melting Onset (Solidus), °C | 1410 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 47 | |
| 15 |
| Thermal Expansion, µm/m-K | 13 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 9.5 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.4 |
| Embodied Energy, MJ/kg | 21 | |
| 33 |
| Embodied Water, L/kg | 50 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 | |
| 93 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 980 | |
| 520 to 1000 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 25 | |
| 28 to 31 |
| Strength to Weight: Bending, points | 23 | |
| 25 to 26 |
| Thermal Diffusivity, mm2/s | 13 | |
| 4.0 |
| Thermal Shock Resistance, points | 21 | |
| 28 to 30 |
Alloy Composition
| Carbon (C), % | 0.070 to 0.12 | |
| 0.33 to 0.45 |
| Chromium (Cr), % | 0 | |
| 15.5 to 17.5 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 95.2 to 97.4 | |
| 77.2 to 83.4 |
| Manganese (Mn), % | 1.6 to 2.1 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0.4 to 0.6 | |
| 0.8 to 1.3 |
| Nickel (Ni), % | 0 to 0.15 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.5 to 0.8 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |
| Residuals, % | 0 to 0.5 | |
| 0 |