AWS ERNiCr-3 vs. CC765S Brass

AWS ERNiCr-3 belongs to the nickel alloys classification, while CC765S brass belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCr-3 and the bottom bar is CC765S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 34
21
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 75
42
Tensile Strength: Ultimate (UTS), MPa 630
540

Thermal Properties

Latent Heat of Fusion, J/g 320
180
Melting Completion (Liquidus), °C 1380
860
Melting Onset (Solidus), °C 1330
820
Specific Heat Capacity, J/kg-K 460
400
Thermal Expansion, µm/m-K 13
20

Otherwise Unclassified Properties

Base Metal Price, % relative 70
24
Density, g/cm3 8.4
8.0
Embodied Carbon, kg CO2/kg material 11
3.0
Embodied Energy, MJ/kg 160
51
Embodied Water, L/kg 280
330

Common Calculations

Stiffness to Weight: Axial, points 13
7.6
Stiffness to Weight: Bending, points 23
20
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 19
18
Thermal Shock Resistance, points 18
17

Alloy Composition

Aluminum (Al), % 0
0.5 to 2.5
Antimony (Sb), % 0
0 to 0.080
Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 18 to 22
0
Cobalt (Co), % 0 to 0.12
0
Copper (Cu), % 0 to 0.5
51 to 65
Iron (Fe), % 0 to 3.0
0.5 to 2.0
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 2.5 to 3.5
0.3 to 3.0
Nickel (Ni), % 67 to 77.5
0 to 6.0
Niobium (Nb), % 2.0 to 3.0
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.5
0 to 0.1
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 1.0
Titanium (Ti), % 0 to 0.75
0
Zinc (Zn), % 0
19.8 to 47.7
Residuals, % 0 to 0.5
0