AWS ERNiCr-3 vs. C19000 Copper
AWS ERNiCr-3 belongs to the nickel alloys classification, while C19000 copper belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS ERNiCr-3 and the bottom bar is C19000 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 34 | |
| 2.5 to 50 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 75 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 260 to 760 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 210 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1080 |
| Melting Onset (Solidus), °C | 1330 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 390 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 31 |
| Density, g/cm3 | 8.4 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 2.7 |
| Embodied Energy, MJ/kg | 160 | |
| 42 |
| Embodied Water, L/kg | 280 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 23 | |
| 18 |
| Strength to Weight: Axial, points | 21 | |
| 8.2 to 24 |
| Strength to Weight: Bending, points | 19 | |
| 10 to 21 |
| Thermal Shock Resistance, points | 18 | |
| 9.3 to 27 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 18 to 22 | |
| 0 |
| Cobalt (Co), % | 0 to 0.12 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 96.9 to 99 |
| Iron (Fe), % | 0 to 3.0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 2.5 to 3.5 | |
| 0 |
| Nickel (Ni), % | 67 to 77.5 | |
| 0.9 to 1.3 |
| Niobium (Nb), % | 2.0 to 3.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0.15 to 0.35 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0 to 0.75 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.8 |
| Residuals, % | 0 | |
| 0 to 0.5 |