AWS ERNiCrCoMo-1 vs. Solder Alloy 141

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while solder alloy 141 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is solder alloy 141.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
37
Elongation at Break, % 28
39
Poisson's Ratio 0.29
0.39
Shear Modulus, GPa 81
13
Tensile Strength: Ultimate (UTS), MPa 710
54

Thermal Properties

Latent Heat of Fusion, J/g 330
46
Melting Completion (Liquidus), °C 1420
190
Melting Onset (Solidus), °C 1370
180
Specific Heat Capacity, J/kg-K 450
180
Thermal Conductivity, W/m-K 13
48
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
10
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
10

Otherwise Unclassified Properties

Density, g/cm3 8.5
8.9
Embodied Carbon, kg CO2/kg material 10
11
Embodied Energy, MJ/kg 140
180
Embodied Water, L/kg 350
970

Common Calculations

Stiffness to Weight: Axial, points 14
2.3
Stiffness to Weight: Bending, points 23
13
Strength to Weight: Axial, points 23
1.7
Strength to Weight: Bending, points 21
3.6
Thermal Diffusivity, mm2/s 3.5
29
Thermal Shock Resistance, points 19
4.3

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
2.0 to 3.0
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.050 to 0.15
0
Chromium (Cr), % 20 to 24
0
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 0 to 3.0
0 to 0.020
Lead (Pb), % 0
35.9 to 38.5
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 42.7 to 61.2
0 to 0.010
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
59.5 to 60.5
Titanium (Ti), % 0 to 0.6
0
Zinc (Zn), % 0
0 to 0.0010
Residuals, % 0 to 0.5
0