AWS ERNiCrCoMo-1 vs. S44625 Stainless Steel

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while S44625 stainless steel belongs to the iron alloys. They have a modest 25% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is S44625 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 28
22
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 81
80
Tensile Strength: Ultimate (UTS), MPa 710
590

Thermal Properties

Latent Heat of Fusion, J/g 330
290
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 450
480
Thermal Conductivity, W/m-K 13
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 75
14
Density, g/cm3 8.5
7.7
Embodied Carbon, kg CO2/kg material 10
2.8
Embodied Energy, MJ/kg 140
39
Embodied Water, L/kg 350
160

Common Calculations

Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 23
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 3.5
4.6
Thermal Shock Resistance, points 19
19

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0
Carbon (C), % 0.050 to 0.15
0 to 0.010
Chromium (Cr), % 20 to 24
25 to 27.5
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0 to 0.2
Iron (Fe), % 0 to 3.0
69.4 to 74.3
Manganese (Mn), % 0 to 1.0
0 to 0.4
Molybdenum (Mo), % 8.0 to 10
0.75 to 1.5
Nickel (Ni), % 42.7 to 61.2
0 to 0.5
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 0 to 0.6
0
Residuals, % 0 to 0.5
0