AWS ERNiCrFe-5 vs. SAE-AISI 1144 Steel

AWS ERNiCrFe-5 belongs to the nickel alloys classification, while SAE-AISI 1144 steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-5 and the bottom bar is SAE-AISI 1144 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 34
11 to 17
Poisson's Ratio 0.3
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 630
750 to 840

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1390
1450
Melting Onset (Solidus), °C 1340
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 14
51
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.6
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.7
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 65
1.9
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 11
1.4
Embodied Energy, MJ/kg 150
19
Embodied Water, L/kg 250
47

Common Calculations

Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 20
27 to 30
Strength to Weight: Bending, points 19
23 to 25
Thermal Diffusivity, mm2/s 3.6
14
Thermal Shock Resistance, points 19
22 to 24

Alloy Composition

Carbon (C), % 0 to 0.080
0.4 to 0.48
Chromium (Cr), % 14 to 17
0
Cobalt (Co), % 0 to 0.12
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 6.0 to 10
97.5 to 98
Manganese (Mn), % 0 to 1.0
1.4 to 1.7
Nickel (Ni), % 70 to 78.5
0
Niobium (Nb), % 1.5 to 3.0
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.35
0
Sulfur (S), % 0 to 0.015
0.24 to 0.33
Residuals, % 0 to 0.5
0