AWS ERNiCrFe-5 vs. S20910 Stainless Steel
AWS ERNiCrFe-5 belongs to the nickel alloys classification, while S20910 stainless steel belongs to the iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AWS ERNiCrFe-5 and the bottom bar is S20910 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 34 | |
| 14 to 39 |
| Poisson's Ratio | 0.3 | |
| 0.28 |
| Shear Modulus, GPa | 74 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 780 to 940 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 300 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1420 |
| Melting Onset (Solidus), °C | 1340 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 14 | |
| 13 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 22 |
| Density, g/cm3 | 8.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 4.8 |
| Embodied Energy, MJ/kg | 150 | |
| 68 |
| Embodied Water, L/kg | 250 | |
| 180 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 28 to 33 |
| Strength to Weight: Bending, points | 19 | |
| 24 to 27 |
| Thermal Diffusivity, mm2/s | 3.6 | |
| 3.6 |
| Thermal Shock Resistance, points | 19 | |
| 17 to 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.080 | |
| 0 to 0.060 |
| Chromium (Cr), % | 14 to 17 | |
| 20.5 to 23.5 |
| Cobalt (Co), % | 0 to 0.12 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 6.0 to 10 | |
| 52.1 to 62.1 |
| Manganese (Mn), % | 0 to 1.0 | |
| 4.0 to 6.0 |
| Molybdenum (Mo), % | 0 | |
| 1.5 to 3.0 |
| Nickel (Ni), % | 70 to 78.5 | |
| 11.5 to 13.5 |
| Niobium (Nb), % | 1.5 to 3.0 | |
| 0.1 to 0.3 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.4 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.3 |
| Residuals, % | 0 to 0.5 | |
| 0 |