AWS ERNiCrMo-10 vs. AWS BAg-7

AWS ERNiCrMo-10 belongs to the nickel alloys classification, while AWS BAg-7 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrMo-10 and the bottom bar is AWS BAg-7.

AWS ERNiCrMo-10 Weld Metal AWS BAg-7 (P07563) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		83

Poisson's Ratio		0.29
Poisson's Ratio		0.34

Shear Modulus, GPa		84
Shear Modulus, GPa		31

Tensile Strength: Ultimate (UTS), MPa		790
Tensile Strength: Ultimate (UTS), MPa		150

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		130

Melting Completion (Liquidus), °C		1550
Melting Completion (Liquidus), °C		650

Melting Onset (Solidus), °C		1490
Melting Onset (Solidus), °C		620

Specific Heat Capacity, J/kg-K		420
Specific Heat Capacity, J/kg-K		290

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		20

Otherwise Unclassified Properties

Density, g/cm³		8.9
Density, g/cm³		9.3

Embodied Carbon, kg CO₂/kg material		12
Embodied Carbon, kg CO₂/kg material		55

Embodied Energy, MJ/kg		160
Embodied Energy, MJ/kg		860

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		4.9

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		16

Strength to Weight: Axial, points		25
Strength to Weight: Axial, points		4.5

Strength to Weight: Bending, points		21
Strength to Weight: Bending, points		6.7

Thermal Shock Resistance, points		21
Thermal Shock Resistance, points		6.4

Alloy Composition

Carbon (C), %		0 to 0.015
Carbon (C), %		0

Chromium (Cr), %		20 to 22.5
Chromium (Cr), %		0

Cobalt (Co), %		0 to 2.5
Cobalt (Co), %		0

Copper (Cu), %		0 to 0.5
Copper (Cu), %		21 to 23

Iron (Fe), %		2.0 to 6.0
Iron (Fe), %		0

Manganese (Mn), %		0 to 0.5
Manganese (Mn), %		0

Molybdenum (Mo), %		12.5 to 14.5
Molybdenum (Mo), %		0

Nickel (Ni), %		49 to 63
Nickel (Ni), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0

Silicon (Si), %		0 to 0.080
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		55 to 57

Sulfur (S), %		0 to 0.010
Sulfur (S), %		0

Tin (Sn), %		0
Tin (Sn), %		4.5 to 5.5

Tungsten (W), %		2.5 to 3.5
Tungsten (W), %		0

Vanadium (V), %		0 to 0.35
Vanadium (V), %		0

Zinc (Zn), %		0
Zinc (Zn), %		15 to 19

Residuals, %		0
Residuals, %		0 to 0.15