AWS ERNiCrMo-2 vs. EN 1.3536 Steel

AWS ERNiCrMo-2 belongs to the nickel alloys classification, while EN 1.3536 steel belongs to the iron alloys. They have a modest 22% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrMo-2 and the bottom bar is EN 1.3536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 750
660

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 11
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 55
2.9
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 9.2
1.6
Embodied Energy, MJ/kg 120
21
Embodied Water, L/kg 270
55

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 25
23
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 2.9
11
Thermal Shock Resistance, points 20
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.050 to 0.15
0.93 to 1.1
Chromium (Cr), % 20.5 to 23
1.7 to 2.0
Cobalt (Co), % 0.5 to 2.5
0
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 17 to 20
96 to 97.4
Manganese (Mn), % 0 to 1.0
0.6 to 0.8
Molybdenum (Mo), % 8.0 to 10
0.2 to 0.35
Nickel (Ni), % 40.3 to 53.8
0
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.15 to 0.45
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.2 to 1.0
0
Residuals, % 0 to 0.5
0