AWS ERNiCrMo-2 vs. EN 1.4347 Stainless Steel

AWS ERNiCrMo-2 belongs to the nickel alloys classification, while EN 1.4347 stainless steel belongs to the iron alloys. They have 48% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrMo-2 and the bottom bar is EN 1.4347 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 81
79
Tensile Strength: Ultimate (UTS), MPa 750
660

Thermal Properties

Latent Heat of Fusion, J/g 320
300
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1410
1370
Specific Heat Capacity, J/kg-K 450
490
Thermal Conductivity, W/m-K 11
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.5
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.6
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 55
16
Density, g/cm3 8.4
7.7
Embodied Carbon, kg CO2/kg material 9.2
3.1
Embodied Energy, MJ/kg 120
44
Embodied Water, L/kg 270
170

Common Calculations

Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 25
24
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 2.9
4.0
Thermal Shock Resistance, points 20
19

Alloy Composition

Carbon (C), % 0.050 to 0.15
0 to 0.050
Chromium (Cr), % 20.5 to 23
25 to 27
Cobalt (Co), % 0.5 to 2.5
0
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 17 to 20
62.2 to 69.4
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 8.0 to 10
0
Nickel (Ni), % 40.3 to 53.8
5.5 to 7.5
Nitrogen (N), % 0
0.1 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.020
Tungsten (W), % 0.2 to 1.0
0
Residuals, % 0 to 0.5
0