AWS ERNiCrMo-4 vs. C63200 Bronze
AWS ERNiCrMo-4 belongs to the nickel alloys classification, while C63200 bronze belongs to the copper alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS ERNiCrMo-4 and the bottom bar is C63200 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 120 |
| Elongation at Break, % | 28 | |
| 17 to 18 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 84 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 790 | |
| 640 to 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 230 |
| Melting Completion (Liquidus), °C | 1590 | |
| 1060 |
| Melting Onset (Solidus), °C | 1530 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 440 |
| Thermal Expansion, µm/m-K | 12 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 29 |
| Density, g/cm3 | 9.0 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 13 | |
| 3.4 |
| Embodied Energy, MJ/kg | 170 | |
| 55 |
| Embodied Water, L/kg | 280 | |
| 380 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.9 |
| Stiffness to Weight: Bending, points | 22 | |
| 20 |
| Strength to Weight: Axial, points | 24 | |
| 21 to 24 |
| Strength to Weight: Bending, points | 21 | |
| 20 to 21 |
| Thermal Shock Resistance, points | 22 | |
| 22 to 24 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 8.7 to 9.5 |
| Carbon (C), % | 0 to 0.020 | |
| 0 |
| Chromium (Cr), % | 14.5 to 16.5 | |
| 0 |
| Cobalt (Co), % | 0 to 2.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 78.8 to 82.6 |
| Iron (Fe), % | 4.0 to 7.0 | |
| 3.5 to 4.3 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 1.0 | |
| 1.2 to 2.0 |
| Molybdenum (Mo), % | 15 to 17 | |
| 0 |
| Nickel (Ni), % | 50 to 63.5 | |
| 4.0 to 4.8 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.080 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tungsten (W), % | 3.0 to 4.5 | |
| 0 |
| Vanadium (V), % | 0 to 0.35 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |