AWS ERNiCu-7 vs. N12160 Nickel
Both AWS ERNiCu-7 and N12160 nickel are nickel alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AWS ERNiCu-7 and the bottom bar is N12160 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 210 |
| Elongation at Break, % | 34 | |
| 45 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 61 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 550 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 360 |
| Melting Completion (Liquidus), °C | 1280 | |
| 1330 |
| Melting Onset (Solidus), °C | 1240 | |
| 1280 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 470 |
| Thermal Conductivity, W/m-K | 20 | |
| 11 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 90 |
| Density, g/cm3 | 8.7 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 8.5 | |
| 8.5 |
| Embodied Energy, MJ/kg | 120 | |
| 120 |
| Embodied Water, L/kg | 250 | |
| 400 |
Common Calculations
| Stiffness to Weight: Axial, points | 10 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 18 | |
| 24 |
| Strength to Weight: Bending, points | 17 | |
| 22 |
| Thermal Diffusivity, mm2/s | 5.3 | |
| 2.8 |
| Thermal Shock Resistance, points | 19 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0 to 1.3 | |
| 0 |
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 26 to 30 |
| Cobalt (Co), % | 0 | |
| 27 to 33 |
| Copper (Cu), % | 18.3 to 36.5 | |
| 0 |
| Iron (Fe), % | 0 to 2.5 | |
| 0 to 3.5 |
| Manganese (Mn), % | 0 to 4.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 62 to 69 | |
| 25 to 44.4 |
| Niobium (Nb), % | 0 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.3 | |
| 2.4 to 3.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.015 |
| Titanium (Ti), % | 1.5 to 3.0 | |
| 0.2 to 0.8 |
| Tungsten (W), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 to 0.5 | |
| 0 |