AWS ERTi-1 vs. S44735 Stainless Steel
AWS ERTi-1 belongs to the titanium alloys classification, while S44735 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS ERTi-1 and the bottom bar is S44735 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 110 | |
210 |
Elongation at Break, % | 24 | |
21 |
Fatigue Strength, MPa | 120 | |
300 |
Poisson's Ratio | 0.32 | |
0.27 |
Shear Modulus, GPa | 41 | |
82 |
Tensile Strength: Ultimate (UTS), MPa | 240 | |
630 |
Tensile Strength: Yield (Proof), MPa | 170 | |
460 |
Thermal Properties
Latent Heat of Fusion, J/g | 420 | |
310 |
Maximum Temperature: Mechanical, °C | 320 | |
1100 |
Melting Completion (Liquidus), °C | 1670 | |
1460 |
Melting Onset (Solidus), °C | 1620 | |
1420 |
Specific Heat Capacity, J/kg-K | 540 | |
480 |
Thermal Expansion, µm/m-K | 8.7 | |
11 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 37 | |
21 |
Density, g/cm3 | 4.5 | |
7.7 |
Embodied Carbon, kg CO2/kg material | 31 | |
4.4 |
Embodied Energy, MJ/kg | 510 | |
61 |
Embodied Water, L/kg | 110 | |
180 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 52 | |
120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
520 |
Stiffness to Weight: Axial, points | 13 | |
15 |
Stiffness to Weight: Bending, points | 35 | |
26 |
Strength to Weight: Axial, points | 15 | |
23 |
Strength to Weight: Bending, points | 19 | |
21 |
Thermal Shock Resistance, points | 19 | |
20 |
Alloy Composition
Carbon (C), % | 0 to 0.030 | |
0 to 0.030 |
Chromium (Cr), % | 0 | |
28 to 30 |
Hydrogen (H), % | 0 to 0.0050 | |
0 |
Iron (Fe), % | 0 to 0.080 | |
60.7 to 68.4 |
Manganese (Mn), % | 0 | |
0 to 1.0 |
Molybdenum (Mo), % | 0 | |
3.6 to 4.2 |
Nickel (Ni), % | 0 | |
0 to 1.0 |
Niobium (Nb), % | 0 | |
0.2 to 1.0 |
Nitrogen (N), % | 0 to 0.012 | |
0 to 0.045 |
Oxygen (O), % | 0.030 to 0.1 | |
0 |
Phosphorus (P), % | 0 | |
0 to 0.040 |
Silicon (Si), % | 0 | |
0 to 1.0 |
Sulfur (S), % | 0 | |
0 to 0.030 |
Titanium (Ti), % | 99.773 to 99.97 | |
0.2 to 1.0 |