AWS ERTi-12 vs. EN 1.3967 Stainless Steel
AWS ERTi-12 belongs to the titanium alloys classification, while EN 1.3967 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AWS ERTi-12 and the bottom bar is EN 1.3967 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 12 | |
| 22 |
| Fatigue Strength, MPa | 200 | |
| 240 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 41 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 480 | |
| 690 |
| Tensile Strength: Yield (Proof), MPa | 340 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 1070 |
| Melting Completion (Liquidus), °C | 1670 | |
| 1430 |
| Melting Onset (Solidus), °C | 1620 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 470 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 25 |
| Density, g/cm3 | 4.5 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 31 | |
| 4.8 |
| Embodied Energy, MJ/kg | 510 | |
| 66 |
| Embodied Water, L/kg | 110 | |
| 180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 52 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 | |
| 310 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 35 | |
| 25 |
| Strength to Weight: Axial, points | 30 | |
| 24 |
| Strength to Weight: Bending, points | 30 | |
| 22 |
| Thermal Shock Resistance, points | 37 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 20 to 21.5 |
| Hydrogen (H), % | 0 to 0.0080 | |
| 0 |
| Iron (Fe), % | 0 to 0.15 | |
| 50.3 to 57.8 |
| Manganese (Mn), % | 0 | |
| 4.0 to 6.0 |
| Molybdenum (Mo), % | 0.2 to 0.4 | |
| 3.0 to 3.5 |
| Nickel (Ni), % | 0.060 to 0.090 | |
| 15 to 17 |
| Niobium (Nb), % | 0 | |
| 0 to 0.25 |
| Nitrogen (N), % | 0 to 0.015 | |
| 0.2 to 0.35 |
| Oxygen (O), % | 0.080 to 0.16 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 99.147 to 99.66 | |
| 0 |