AWS ERTi-12 vs. EN AC-21100 Aluminum
AWS ERTi-12 belongs to the titanium alloys classification, while EN AC-21100 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is AWS ERTi-12 and the bottom bar is EN AC-21100 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 71 |
| Elongation at Break, % | 12 | |
| 6.2 to 7.3 |
| Fatigue Strength, MPa | 200 | |
| 79 to 87 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 41 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 480 | |
| 340 to 350 |
| Tensile Strength: Yield (Proof), MPa | 340 | |
| 210 to 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 170 |
| Melting Completion (Liquidus), °C | 1670 | |
| 670 |
| Melting Onset (Solidus), °C | 1620 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 880 |
| Thermal Conductivity, W/m-K | 21 | |
| 130 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.6 | |
| 34 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.1 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 37 | |
| 11 |
| Density, g/cm3 | 4.5 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 31 | |
| 8.0 |
| Embodied Energy, MJ/kg | 510 | |
| 150 |
| Embodied Water, L/kg | 110 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 52 | |
| 19 to 21 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 | |
| 300 to 400 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 35 | |
| 46 |
| Strength to Weight: Axial, points | 30 | |
| 31 to 33 |
| Strength to Weight: Bending, points | 30 | |
| 36 to 37 |
| Thermal Diffusivity, mm2/s | 8.7 | |
| 48 |
| Thermal Shock Resistance, points | 37 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 93.4 to 95.7 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Copper (Cu), % | 0 | |
| 4.2 to 5.2 |
| Hydrogen (H), % | 0 to 0.0080 | |
| 0 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 to 0.19 |
| Manganese (Mn), % | 0 | |
| 0 to 0.55 |
| Molybdenum (Mo), % | 0.2 to 0.4 | |
| 0 |
| Nickel (Ni), % | 0.060 to 0.090 | |
| 0 |
| Nitrogen (N), % | 0 to 0.015 | |
| 0 |
| Oxygen (O), % | 0.080 to 0.16 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.18 |
| Titanium (Ti), % | 99.147 to 99.66 | |
| 0.15 to 0.3 |
| Zinc (Zn), % | 0 | |
| 0 to 0.070 |
| Residuals, % | 0 | |
| 0 to 0.1 |