MakeItFrom.com
Menu (ESC)

AWS ERTi-7 vs. AWS E347

AWS ERTi-7 belongs to the titanium alloys classification, while AWS E347 belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS ERTi-7 and the bottom bar is AWS E347.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
200
Elongation at Break, % 20
34
Poisson's Ratio 0.32
0.28
Shear Modulus, GPa 40
77
Tensile Strength: Ultimate (UTS), MPa 340
580

Thermal Properties

Latent Heat of Fusion, J/g 420
290
Melting Completion (Liquidus), °C 1670
1430
Melting Onset (Solidus), °C 1620
1380
Specific Heat Capacity, J/kg-K 540
480
Thermal Conductivity, W/m-K 21
16
Thermal Expansion, µm/m-K 8.7
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.6
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 7.3
2.4

Otherwise Unclassified Properties

Density, g/cm3 4.5
7.8
Embodied Carbon, kg CO2/kg material 47
3.7
Embodied Energy, MJ/kg 800
53
Embodied Water, L/kg 470
150

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 35
25
Strength to Weight: Axial, points 21
21
Strength to Weight: Bending, points 24
20
Thermal Diffusivity, mm2/s 8.8
4.2
Thermal Shock Resistance, points 26
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 0
18 to 21
Copper (Cu), % 0
0 to 0.75
Hydrogen (H), % 0 to 0.0080
0
Iron (Fe), % 0 to 0.12
61.9 to 72.5
Manganese (Mn), % 0
0.5 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0
9.0 to 11
Niobium (Nb), % 0
0 to 1.0
Nitrogen (N), % 0 to 0.015
0
Oxygen (O), % 0.080 to 0.16
0
Palladium (Pd), % 0.12 to 0.25
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 99.417 to 99.8
0