AWS ERTi-7 vs. C95400 Bronze
AWS ERTi-7 belongs to the titanium alloys classification, while C95400 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AWS ERTi-7 and the bottom bar is C95400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 20 | |
| 8.1 to 16 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 40 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 340 | |
| 600 to 710 |
| Tensile Strength: Yield (Proof), MPa | 280 | |
| 240 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 320 | |
| 230 |
| Melting Completion (Liquidus), °C | 1670 | |
| 1040 |
| Melting Onset (Solidus), °C | 1620 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 540 | |
| 440 |
| Thermal Conductivity, W/m-K | 21 | |
| 59 |
| Thermal Expansion, µm/m-K | 8.7 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.6 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 4.5 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 47 | |
| 3.2 |
| Embodied Energy, MJ/kg | 800 | |
| 53 |
| Embodied Water, L/kg | 470 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 64 | |
| 48 to 75 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 | |
| 250 to 560 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 35 | |
| 20 |
| Strength to Weight: Axial, points | 21 | |
| 20 to 24 |
| Strength to Weight: Bending, points | 24 | |
| 19 to 22 |
| Thermal Diffusivity, mm2/s | 8.8 | |
| 16 |
| Thermal Shock Resistance, points | 26 | |
| 21 to 25 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 10 to 11.5 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Copper (Cu), % | 0 | |
| 83 to 87 |
| Hydrogen (H), % | 0 to 0.0080 | |
| 0 |
| Iron (Fe), % | 0 to 0.12 | |
| 3.0 to 5.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 0 to 1.5 |
| Nitrogen (N), % | 0 to 0.015 | |
| 0 |
| Oxygen (O), % | 0.080 to 0.16 | |
| 0 |
| Palladium (Pd), % | 0.12 to 0.25 | |
| 0 |
| Titanium (Ti), % | 99.417 to 99.8 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |