AZ80A Magnesium vs. 201.0 Aluminum
AZ80A magnesium belongs to the magnesium alloys classification, while 201.0 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AZ80A magnesium and the bottom bar is 201.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 46 | |
| 71 |
| Elongation at Break, % | 3.9 to 8.5 | |
| 4.4 to 20 |
| Fatigue Strength, MPa | 140 to 170 | |
| 120 to 150 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 18 | |
| 27 |
| Shear Strength, MPa | 160 to 190 | |
| 290 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 340 | |
| 370 to 470 |
| Tensile Strength: Yield (Proof), MPa | 210 to 230 | |
| 220 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 170 |
| Melting Completion (Liquidus), °C | 600 | |
| 650 |
| Melting Onset (Solidus), °C | 490 | |
| 570 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 870 |
| Thermal Conductivity, W/m-K | 77 | |
| 120 |
| Thermal Expansion, µm/m-K | 26 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 30 to 33 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 59 | |
| 87 to 97 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 38 |
| Density, g/cm3 | 1.7 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 8.7 |
| Embodied Energy, MJ/kg | 160 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 24 | |
| 19 to 63 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 500 to 600 | |
| 330 to 1160 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 69 | |
| 45 |
| Strength to Weight: Axial, points | 51 to 55 | |
| 33 to 42 |
| Strength to Weight: Bending, points | 60 to 63 | |
| 37 to 44 |
| Thermal Diffusivity, mm2/s | 45 | |
| 45 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 19 to 25 |
Alloy Composition
| Aluminum (Al), % | 7.8 to 9.2 | |
| 92.1 to 95.1 |
| Copper (Cu), % | 0 to 0.050 | |
| 4.0 to 5.2 |
| Iron (Fe), % | 0 to 0.0050 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 89 to 91.9 | |
| 0.15 to 0.55 |
| Manganese (Mn), % | 0.12 to 0.5 | |
| 0.2 to 0.5 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.1 |
| Silver (Ag), % | 0 | |
| 0.4 to 1.0 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.35 |
| Zinc (Zn), % | 0.2 to 0.8 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.1 |