AZ80A Magnesium vs. 92-silver 8-tin-oxide
AZ80A magnesium belongs to the magnesium alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is AZ80A magnesium and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 76 to 80 |
| Elongation at Break, % | 3.9 to 8.5 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 24 | |
| 62 to 110 |
| Shear Strength, MPa | 160 to 190 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 340 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 210 to 230 | |
| 120 to 300 |