AZ91A Magnesium vs. ZA-27
AZ91A magnesium belongs to the magnesium alloys classification, while ZA-27 belongs to the zinc alloys. There are 32 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AZ91A magnesium and the bottom bar is ZA-27.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 63 | |
| 100 to 120 |
| Compressive (Crushing) Strength, MPa | 160 | |
| 260 to 370 |
| Elastic (Young's, Tensile) Modulus, GPa | 46 | |
| 78 |
| Elongation at Break, % | 5.0 | |
| 2.0 to 4.5 |
| Fatigue Strength, MPa | 99 | |
| 110 to 170 |
| Poisson's Ratio | 0.29 | |
| 0.27 |
| Shear Modulus, GPa | 18 | |
| 31 |
| Shear Strength, MPa | 140 | |
| 230 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 240 | |
| 400 to 430 |
| Tensile Strength: Yield (Proof), MPa | 160 | |
| 260 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 360 | |
| 130 |
| Maximum Temperature: Mechanical, °C | 130 | |
| 120 |
| Melting Completion (Liquidus), °C | 600 | |
| 480 |
| Melting Onset (Solidus), °C | 470 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 530 |
| Thermal Conductivity, W/m-K | 73 | |
| 130 |
| Thermal Expansion, µm/m-K | 26 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 30 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 52 | |
| 53 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 11 |
| Density, g/cm3 | 1.7 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 22 | |
| 4.2 |
| Embodied Energy, MJ/kg | 160 | |
| 80 |
| Embodied Water, L/kg | 990 | |
| 570 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 | |
| 8.1 to 18 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 | |
| 420 to 890 |
| Stiffness to Weight: Axial, points | 15 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 69 | |
| 28 |
| Strength to Weight: Axial, points | 38 | |
| 22 to 24 |
| Strength to Weight: Bending, points | 49 | |
| 24 to 25 |
| Thermal Diffusivity, mm2/s | 42 | |
| 47 |
| Thermal Shock Resistance, points | 14 | |
| 14 to 15 |
Alloy Composition
| Aluminum (Al), % | 8.3 to 9.7 | |
| 25 to 28 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Copper (Cu), % | 0 to 0.1 | |
| 2.0 to 2.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 88.2 to 91.2 | |
| 0.010 to 0.020 |
| Manganese (Mn), % | 0.13 to 0.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.030 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.080 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0.35 to 1.0 | |
| 69.3 to 73 |