AZ91B Magnesium vs. N08366 Stainless Steel

AZ91B magnesium belongs to the magnesium alloys classification, while N08366 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ91B magnesium and the bottom bar is N08366 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
180
Elastic (Young's, Tensile) Modulus, GPa 46
210
Elongation at Break, % 5.0
34
Fatigue Strength, MPa 79
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 18
80
Shear Strength, MPa 140
390
Tensile Strength: Ultimate (UTS), MPa 240
590
Tensile Strength: Yield (Proof), MPa 160
240

Thermal Properties

Latent Heat of Fusion, J/g 360
310
Maximum Temperature: Mechanical, °C 130
1100
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 470
1410
Specific Heat Capacity, J/kg-K 990
460
Thermal Conductivity, W/m-K 73
13
Thermal Expansion, µm/m-K 26
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
1.8
Electrical Conductivity: Equal Weight (Specific), % IACS 58
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
33
Density, g/cm3 1.7
8.1
Embodied Carbon, kg CO2/kg material 22
6.2
Embodied Energy, MJ/kg 160
84
Embodied Water, L/kg 990
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
160
Resilience: Unit (Modulus of Resilience), kJ/m3 280
150
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 69
24
Strength to Weight: Axial, points 38
20
Strength to Weight: Bending, points 49
19
Thermal Diffusivity, mm2/s 42
3.4
Thermal Shock Resistance, points 14
13

Alloy Composition

Aluminum (Al), % 8.3 to 9.7
0
Carbon (C), % 0
0 to 0.035
Chromium (Cr), % 0
20 to 22
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 0
42.4 to 50.5
Magnesium (Mg), % 87.9 to 91.2
0
Manganese (Mn), % 0.13 to 0.5
0 to 2.0
Molybdenum (Mo), % 0
6.0 to 7.0
Nickel (Ni), % 0 to 0.030
23.5 to 25.5
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0.35 to 1.0
0