AZ91E Magnesium vs. 92-silver 8-tin-oxide
AZ91E magnesium belongs to the magnesium alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (29, in this case) are not shown.
For each property being compared, the top bar is AZ91E magnesium and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 to 12 | |
| 76 to 80 |
| Elongation at Break, % | 2.5 to 6.2 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.4 to 12 | |
| 62 to 110 |
| Shear Strength, MPa | 89 to 150 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 260 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 96 to 130 | |
| 120 to 300 |