POM-C vs. PMP
Both POM-C and PMP are thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is POM-C and the bottom bar is PMP.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 0.83 |
| Elastic (Young's, Tensile) Modulus, GPa | 2.8 to 9.7 | |
| 1.1 |
| Elongation at Break, % | 3.0 to 65 | |
| 30 |
| Impact Strength: Notched Izod, J/m | 68 to 69 | |
| 130 |
| Specific Heat Capacity, J/kg-K | 1130 to 1370 | |
| 1750 |
| Stiffness to Weight: Axial, points | 1.1 to 3.3 | |
| 0.74 |
| Stiffness to Weight: Bending, points | 33 to 44 | |
| 41 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 8.0 |
| Strength to Weight: Bending, points | 24 to 32 | |
| 22 |
| Tensile Strength: Ultimate (UTS), MPa | 61 to 110 | |
| 24 |