POM-C vs. PPS
Both POM-C and PPS are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is POM-C and the bottom bar is PPS.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.3 to 1.7 |
| Elongation at Break, % | 3.0 to 65 | |
| 2.5 to 11 |
| Flexural Modulus, GPa | 2.6 to 9.0 | |
| 13 to 17 |
| Flexural Strength, MPa | 83 to 170 | |
| 120 to 190 |
| Impact Strength: Notched Izod, J/m | 68 to 69 | |
| 21 to 80 |
| Specific Heat Capacity, J/kg-K | 1130 to 1370 | |
| 910 to 1000 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 16 to 37 |
| Strength to Weight: Bending, points | 24 to 32 | |
| 30 to 52 |
| Tensile Strength: Ultimate (UTS), MPa | 61 to 110 | |
| 75 to 190 |