POM-C vs. PP Homopolymer
Both POM-C and PP homopolymer are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is POM-C and the bottom bar is PP homopolymer.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 0.91 to 1.2 |
| Elongation at Break, % | 3.0 to 65 | |
| 3.0 to 80 |
| Flexural Modulus, GPa | 2.6 to 9.0 | |
| 1.5 to 7.0 |
| Flexural Strength, MPa | 83 to 170 | |
| 41 to 100 |
| Impact Strength: Notched Izod, J/m | 68 to 69 | |
| 42 to 95 |
| Specific Heat Capacity, J/kg-K | 1130 to 1370 | |
| 1230 to 1900 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 11 to 21 |
| Strength to Weight: Bending, points | 24 to 32 | |
| 27 to 37 |
| Tensile Strength: Ultimate (UTS), MPa | 61 to 110 | |
| 36 to 93 |