POM-C vs. PVF
Both POM-C and PVF are thermoplastics. There are 8 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is POM-C and the bottom bar is PVF.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.4 |
| Flexural Strength, MPa | 83 to 170 | |
| 90 |
| Impact Strength: Notched Izod, J/m | 68 to 69 | |
| 100 |
| Limiting Oxygen Index (LOI), % | 15 | |
| 23 |
| Specific Heat Capacity, J/kg-K | 1130 to 1370 | |
| 1300 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 13 |
| Strength to Weight: Bending, points | 24 to 32 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 61 to 110 | |
| 65 |