POM-C vs. Thermoset PI
POM-C belongs to the thermoplastics classification, while thermoset PI belongs to the thermoset plastics. There are 10 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is POM-C and the bottom bar is thermoset PI.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 1.4 to 1.6 |
| Elongation at Break, % | 3.0 to 65 | |
| 2.0 to 5.9 |
| Flexural Modulus, GPa | 2.6 to 9.0 | |
| 3.1 to 4.8 |
| Flexural Strength, MPa | 83 to 170 | |
| 60 to 100 |
| Impact Strength: Notched Izod, J/m | 68 to 69 | |
| 21 to 43 |
| Limiting Oxygen Index (LOI), % | 15 | |
| 40 |
| Specific Heat Capacity, J/kg-K | 1130 to 1370 | |
| 1130 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 6.5 to 16 |
| Strength to Weight: Bending, points | 24 to 32 | |
| 16 to 30 |
| Tensile Strength: Ultimate (UTS), MPa | 61 to 110 | |
| 37 to 81 |