POM-C vs. UHMW-PE
Both POM-C and UHMW-PE are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is POM-C and the bottom bar is UHMW-PE.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.4 to 1.6 | |
| 0.94 |
| Elastic (Young's, Tensile) Modulus, GPa | 2.8 to 9.7 | |
| 0.8 |
| Elongation at Break, % | 3.0 to 65 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 1130 to 1370 | |
| 1750 |
| Stiffness to Weight: Axial, points | 1.1 to 3.3 | |
| 0.47 |
| Stiffness to Weight: Bending, points | 33 to 44 | |
| 33 |
| Strength to Weight: Axial, points | 12 to 19 | |
| 14 |
| Strength to Weight: Bending, points | 24 to 32 | |
| 32 |
| Tensile Strength: Ultimate (UTS), MPa | 61 to 110 | |
| 49 |