ABS vs. PVF
Both ABS and PVF are thermoplastics. There are 9 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is ABS and the bottom bar is PVF.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.0 to 1.4 | |
| 1.4 |
| Flexural Strength, MPa | 72 to 97 | |
| 90 |
| Heat Deflection Temperature At 1.82 MPa (264 psi), °C | 76 to 110 | |
| 90 |
| Impact Strength: Notched Izod, J/m | 70 to 370 | |
| 100 |
| Rockwell R Hardness | 100 to 110 | |
| 83 |
| Strength to Weight: Axial, points | 10 to 22 | |
| 13 |
| Strength to Weight: Bending, points | 24 to 37 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 37 to 110 | |
| 65 |
| Thermal Expansion, µm/m-K | 81 to 95 | |
| 100 |