Aluminum Nitride vs. Beryllia
Aluminum nitride belongs to the non-oxide engineering ceramics classification, while beryllia belongs to the oxide-based engineering ceramics. There are 16 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is aluminum nitride and the bottom bar is beryllia.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 2100 | |
| 1650 |
| Elastic (Young's, Tensile) Modulus, GPa | 330 | |
| 350 |
| Flexural Strength, MPa | 190 to 400 | |
| 240 |
| Poisson's Ratio | 0.21 to 0.31 | |
| 0.26 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1380 | |
| 1750 |
| Specific Heat Capacity, J/kg-K | 780 | |
| 1050 |
| Thermal Conductivity, W/m-K | 80 to 190 | |
| 270 |
| Thermal Expansion, µm/m-K | 4.2 to 5.4 | |
| 8.0 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 6.9 to 28 | |
| 6.6 |
| Dielectric Strength (Breakdown Potential), kV/mm | 15 to 56 | |
| 11 |
| Electrical Dissipation At 1 MHz | 0.00020 to 0.0010 | |
| 0.00060 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 to 12 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.9 to 3.3 | |
| 2.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 55 to 63 | |
| 67 |
| Stiffness to Weight: Bending, points | 69 to 80 | |
| 82 |
| Thermal Diffusivity, mm2/s | 31 to 74 | |
| 89 |