Aluminum Nitride vs. Glass-bonded Mica
Aluminum nitride belongs to the non-oxide engineering ceramics classification, while glass-bonded mica belongs to the glass and glass-ceramics. There are 16 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is aluminum nitride and the bottom bar is glass-bonded mica.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 2100 | |
| 270 |
| Elastic (Young's, Tensile) Modulus, GPa | 330 | |
| 71 |
| Flexural Strength, MPa | 190 to 400 | |
| 79 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1380 | |
| 450 |
| Maximum Thermal Shock, °C | 220 | |
| 110 |
| Specific Heat Capacity, J/kg-K | 780 | |
| 500 |
| Thermal Conductivity, W/m-K | 80 to 190 | |
| 23 |
| Thermal Expansion, µm/m-K | 4.2 to 5.4 | |
| 6.7 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 6.9 to 28 | |
| 6.8 |
| Dielectric Strength (Breakdown Potential), kV/mm | 15 to 56 | |
| 20 |
| Electrical Dissipation At 1 MHz | 0.00020 to 0.0010 | |
| 0.0016 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 to 12 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.9 to 3.3 | |
| 2.6 |
Common Calculations
| Stiffness to Weight: Axial, points | 55 to 63 | |
| 15 |
| Stiffness to Weight: Bending, points | 69 to 80 | |
| 52 |
| Thermal Diffusivity, mm2/s | 31 to 74 | |
| 18 |