Aluminum Titanate vs. C-820 Magnesia Ceramic
Both aluminum titanate and C-820 magnesia ceramic are oxide-based engineering ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is aluminum titanate and the bottom bar is C-820 magnesia ceramic.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.2 | |
| 2.7 |
| Elastic (Young's, Tensile) Modulus, GPa | 13 | |
| 100 |
| Flexural Strength, MPa | 29 | |
| 53 |
| Stiffness to Weight: Axial, points | 2.2 | |
| 21 |
| Stiffness to Weight: Bending, points | 24 | |
| 58 |
| Thermal Conductivity, W/m-K | 1.6 | |
| 8.0 |
| Thermal Expansion, µm/m-K | 2.9 | |
| 11 |