Annealed ASTM B541 vs. Annealed Palladium
Both annealed ASTM B541 and annealed palladium are otherwise unclassified metals. Both are furnished in the annealed condition. There are 20 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is annealed ASTM B541 and the bottom bar is annealed palladium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 14 | |
| 11 |
| Knoop Hardness | 220 | |
| 68 |
| Poisson's Ratio | 0.4 | |
| 0.39 |
| Shear Modulus, GPa | 38 | |
| 43 |
| Shear Strength, MPa | 410 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 670 | |
| 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 90 | |
| 160 |
| Melting Completion (Liquidus), °C | 1110 | |
| 1550 |
| Melting Onset (Solidus), °C | 930 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 170 | |
| 240 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 16 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 4.0 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 12 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.4 | |
| 5.6 |
| Stiffness to Weight: Bending, points | 9.0 | |
| 14 |
| Strength to Weight: Axial, points | 11 | |
| 4.5 |
| Strength to Weight: Bending, points | 9.8 | |
| 6.2 |
| Thermal Shock Resistance, points | 36 | |
| 9.8 |
Alloy Composition
| Copper (Cu), % | 13.5 to 15.5 | |
| 0 |
| Gold (Au), % | 70.5 to 72.5 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 99.8 to 100 |
| Platinum (Pt), % | 8.0 to 9.0 | |
| 0 |
| Silver (Ag), % | 4.0 to 5.0 | |
| 0 |
| Zinc (Zn), % | 0.7 to 1.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |