Annealed ASTM B628 vs. Annealed SAE-AISI H41

Annealed ASTM B628 belongs to the otherwise unclassified metals classification, while annealed SAE-AISI H41 belongs to the iron alloys. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is annealed ASTM B628 and the bottom bar is annealed SAE-AISI H41.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 83
200
Poisson's Ratio 0.36
0.29
Shear Modulus, GPa 31
77
Tensile Strength: Ultimate (UTS), MPa 350
710

Thermal Properties

Latent Heat of Fusion, J/g 140
270
Melting Completion (Liquidus), °C 780
1560
Melting Onset (Solidus), °C 780
1510
Specific Heat Capacity, J/kg-K 280
450
Thermal Expansion, µm/m-K 19
12

Otherwise Unclassified Properties

Density, g/cm3 10
8.1

Common Calculations

Stiffness to Weight: Axial, points 4.6
14
Stiffness to Weight: Bending, points 14
24
Strength to Weight: Axial, points 9.5
24
Strength to Weight: Bending, points 11
22
Thermal Shock Resistance, points 16
20

Alloy Composition

Aluminum (Al), % 0 to 0.0050
0
Cadmium (Cd), % 0 to 0.050
0
Carbon (C), % 0
0.6 to 0.75
Chromium (Cr), % 0
3.5 to 4.0
Copper (Cu), % 26.6 to 29
0
Iron (Fe), % 0 to 0.050
81.8 to 85
Lead (Pb), % 0 to 0.030
0
Manganese (Mn), % 0
0.15 to 0.4
Molybdenum (Mo), % 0
8.2 to 9.2
Nickel (Ni), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0
0.2 to 0.45
Silver (Ag), % 71 to 73
0
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
1.4 to 2.1
Vanadium (V), % 0
1.0 to 1.3
Zinc (Zn), % 0 to 0.060
0
Residuals, % 0 to 0.21
0