Annealed SAE-AISI M52 vs. Annealed Nickel 200

Annealed SAE-AISI M52 belongs to the iron alloys classification, while annealed nickel 200 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is annealed SAE-AISI M52 and the bottom bar is annealed nickel 200.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
110
Elastic (Young's, Tensile) Modulus, GPa 190
180
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 75
70
Tensile Strength: Ultimate (UTS), MPa 710
420

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Melting Completion (Liquidus), °C 1510
1460
Melting Onset (Solidus), °C 1470
1440
Specific Heat Capacity, J/kg-K 460
450
Thermal Conductivity, W/m-K 31
69
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.9
18
Electrical Conductivity: Equal Weight (Specific), % IACS 10
18

Otherwise Unclassified Properties

Base Metal Price, % relative 12
65
Density, g/cm3 7.9
8.9
Embodied Carbon, kg CO2/kg material 7.5
11
Embodied Energy, MJ/kg 110
150
Embodied Water, L/kg 89
230

Common Calculations

Stiffness to Weight: Axial, points 14
11
Stiffness to Weight: Bending, points 24
21
Strength to Weight: Axial, points 25
13
Strength to Weight: Bending, points 22
14
Thermal Diffusivity, mm2/s 8.4
17
Thermal Shock Resistance, points 21
13

Alloy Composition

Carbon (C), % 0.85 to 1.0
0 to 0.15
Chromium (Cr), % 3.5 to 4.3
0
Copper (Cu), % 0 to 0.25
0 to 0.25
Iron (Fe), % 84.4 to 88.9
0 to 0.4
Manganese (Mn), % 0.15 to 0.45
0 to 0.35
Molybdenum (Mo), % 4.0 to 4.9
0
Nickel (Ni), % 0 to 0.3
99 to 100
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.2 to 0.6
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.010
Tungsten (W), % 0.75 to 1.5
0
Vanadium (V), % 1.7 to 2.3
0