Annealed Nickel 601 vs. Annealed SAE-AISI T4
Annealed nickel 601 belongs to the nickel alloys classification, while annealed SAE-AISI T4 belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is annealed nickel 601 and the bottom bar is annealed SAE-AISI T4.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1810 |
| Melting Onset (Solidus), °C | 1360 | |
| 1750 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 410 |
| Thermal Conductivity, W/m-K | 11 | |
| 21 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 49 | |
| 55 |
| Density, g/cm3 | 8.3 | |
| 9.4 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 8.5 |
| Embodied Energy, MJ/kg | 110 | |
| 130 |
| Embodied Water, L/kg | 280 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 12 |
| Stiffness to Weight: Bending, points | 23 | |
| 21 |
| Strength to Weight: Axial, points | 22 | |
| 24 |
| Strength to Weight: Bending, points | 20 | |
| 20 |
| Thermal Diffusivity, mm2/s | 2.8 | |
| 5.4 |
| Thermal Shock Resistance, points | 17 | |
| 24 |
Alloy Composition
| Aluminum (Al), % | 1.0 to 1.7 | |
| 0 |
| Carbon (C), % | 0 to 0.1 | |
| 0.7 to 0.8 |
| Chromium (Cr), % | 21 to 25 | |
| 3.8 to 4.5 |
| Cobalt (Co), % | 0 | |
| 4.3 to 5.8 |
| Copper (Cu), % | 0 to 1.0 | |
| 0 to 0.25 |
| Iron (Fe), % | 7.7 to 20 | |
| 66.3 to 72.3 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.1 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 0.4 to 1.0 |
| Nickel (Ni), % | 58 to 63 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 0.2 to 0.4 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 17.5 to 19 |
| Vanadium (V), % | 0 | |
| 0.8 to 1.2 |