Austempered Cast Iron vs. ASTM A216 Cast Steel
Both austempered cast iron and ASTM A216 cast steel are iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is austempered cast iron and the bottom bar is ASTM A216 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 190 |
| Elongation at Break, % | 1.1 to 13 | |
| 25 to 27 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 62 to 69 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 860 to 1800 | |
| 500 to 570 |
| Tensile Strength: Yield (Proof), MPa | 560 to 1460 | |
| 230 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1450 to 1460 |
| Melting Onset (Solidus), °C | 1340 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 470 |
| Thermal Conductivity, W/m-K | 42 | |
| 49 to 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.9 | |
| 1.8 |
| Density, g/cm3 | 7.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 25 | |
| 18 |
| Embodied Water, L/kg | 48 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 to 95 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 880 to 3970 | |
| 140 to 250 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 32 to 66 | |
| 18 to 20 |
| Strength to Weight: Bending, points | 27 to 44 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 13 to 14 |
| Thermal Shock Resistance, points | 25 to 53 | |
| 16 to 18 |