Austenitic Grey Cast Iron vs. S13800 Stainless Steel

Both austenitic grey cast iron and S13800 stainless steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is austenitic grey cast iron and the bottom bar is S13800 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 210
290 to 480
Elastic (Young's, Tensile) Modulus, GPa 180
200
Poisson's Ratio 0.29 to 0.3
0.28
Shear Modulus, GPa 69 to 72
77
Tensile Strength: Ultimate (UTS), MPa 150 to 230
980 to 1730

Thermal Properties

Latent Heat of Fusion, J/g 280 to 350
280
Melting Completion (Liquidus), °C 1340 to 1400
1450
Melting Onset (Solidus), °C 1290 to 1350
1410
Specific Heat Capacity, J/kg-K 470 to 490
470
Thermal Expansion, µm/m-K 13 to 14
11

Otherwise Unclassified Properties

Base Metal Price, % relative 14 to 24
15
Density, g/cm3 7.7 to 8.1
7.9
Embodied Carbon, kg CO2/kg material 3.1 to 4.7
3.4
Embodied Energy, MJ/kg 43 to 65
46
Embodied Water, L/kg 93 to 120
140

Common Calculations

PREN (Pitting Resistance) 2.0 to 5.0
21
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23 to 25
25
Strength to Weight: Axial, points 5.3 to 8.2
35 to 61
Strength to Weight: Bending, points 7.9 to 11
28 to 41
Thermal Shock Resistance, points 4.5 to 6.5
33 to 58