Austenitic Grey Cast Iron vs. Z41321 Zinc
Austenitic grey cast iron belongs to the iron alloys classification, while Z41321 zinc belongs to the zinc alloys. There are 19 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is austenitic grey cast iron and the bottom bar is Z41321 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 87 |
| Poisson's Ratio | 0.29 to 0.3 | |
| 0.25 |
| Shear Modulus, GPa | 69 to 72 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 150 to 230 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 to 350 | |
| 110 |
| Melting Completion (Liquidus), °C | 1340 to 1400 | |
| 410 |
| Melting Onset (Solidus), °C | 1290 to 1350 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 470 to 490 | |
| 390 |
| Thermal Expansion, µm/m-K | 13 to 14 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 to 24 | |
| 12 |
| Density, g/cm3 | 7.7 to 8.1 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 3.1 to 4.7 | |
| 2.8 |
| Embodied Energy, MJ/kg | 43 to 65 | |
| 54 |
| Embodied Water, L/kg | 93 to 120 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 23 to 25 | |
| 23 |
| Strength to Weight: Axial, points | 5.3 to 8.2 | |
| 7.9 |
| Strength to Weight: Bending, points | 7.9 to 11 | |
| 11 |
| Thermal Shock Resistance, points | 4.5 to 6.5 | |
| 5.9 |