Austenitic Nodular Cast Iron vs. 92-silver 8-tin-oxide
Austenitic nodular cast iron belongs to the iron alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 4 material properties with values for both materials. Properties with values for just one material (22, in this case) are not shown.
For each property being compared, the top bar is austenitic nodular cast iron and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Elongation at Break, % | 6.8 to 34 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 140 | |
| 62 to 110 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 500 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 190 to 240 | |
| 120 to 300 |