Austenitic Nodular Cast Iron vs. ASTM B477 Au-Ni-Ag
Austenitic nodular cast iron belongs to the iron alloys classification, while ASTM B477 Au-Ni-Ag belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is austenitic nodular cast iron and the bottom bar is ASTM B477 Au-Ni-Ag.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 to 190 | |
| 95 |
| Elongation at Break, % | 6.8 to 34 | |
| 5.5 to 11 |
| Poisson's Ratio | 0.29 to 0.3 | |
| 0.41 |
| Shear Modulus, GPa | 70 to 72 | |
| 34 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 500 | |
| 310 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 to 350 | |
| 80 |
| Melting Completion (Liquidus), °C | 1340 to 1400 | |
| 1010 |
| Melting Onset (Solidus), °C | 1300 to 1360 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 470 to 490 | |
| 160 |
| Thermal Expansion, µm/m-K | 13 to 14 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 to 8.0 | |
| 17 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 3.1 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 8.9 |
| Strength to Weight: Axial, points | 15 to 18 | |
| 5.0 to 9.0 |
| Strength to Weight: Bending, points | 16 to 18 | |
| 6.0 to 8.8 |
| Thermal Shock Resistance, points | 12 to 15 | |
| 16 to 28 |