Austenitic Nodular Cast Iron vs. ASTM B631 Class A
Austenitic nodular cast iron belongs to the iron alloys classification, while ASTM B631 class A belongs to the otherwise unclassified metals. There are 12 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is austenitic nodular cast iron and the bottom bar is ASTM B631 class A.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 to 190 | |
| 220 |
| Poisson's Ratio | 0.29 to 0.3 | |
| 0.3 |
| Shear Modulus, GPa | 70 to 72 | |
| 85 to 86 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 to 350 | |
| 160 |
| Melting Completion (Liquidus), °C | 1340 to 1400 | |
| 2680 to 2690 |
| Specific Heat Capacity, J/kg-K | 470 to 490 | |
| 160 |
| Thermal Expansion, µm/m-K | 13 to 14 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 to 8.0 | |
| 15 |
| Embodied Carbon, kg CO2/kg material | 3.5 to 4.9 | |
| 43 |
| Embodied Energy, MJ/kg | 48 to 68 | |
| 670 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 8.5 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 14 |