Austenitic Nodular Cast Iron vs. EN 1.4662 Stainless Steel
Both austenitic nodular cast iron and EN 1.4662 stainless steel are iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is austenitic nodular cast iron and the bottom bar is EN 1.4662 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 to 190 | |
| 200 |
| Elongation at Break, % | 6.8 to 34 | |
| 28 |
| Poisson's Ratio | 0.29 to 0.3 | |
| 0.27 |
| Shear Modulus, GPa | 70 to 72 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 500 | |
| 810 to 830 |
| Tensile Strength: Yield (Proof), MPa | 190 to 240 | |
| 580 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 to 350 | |
| 290 |
| Melting Completion (Liquidus), °C | 1340 to 1400 | |
| 1430 |
| Melting Onset (Solidus), °C | 1300 to 1360 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 to 490 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 to 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 to 25 | |
| 16 |
| Density, g/cm3 | 7.7 to 8.0 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 3.5 to 4.9 | |
| 3.2 |
| Embodied Energy, MJ/kg | 48 to 68 | |
| 45 |
| Embodied Water, L/kg | 91 to 120 | |
| 170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 24 to 140 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 98 to 160 | |
| 840 to 940 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 25 |
| Strength to Weight: Axial, points | 15 to 18 | |
| 29 to 30 |
| Strength to Weight: Bending, points | 16 to 18 | |
| 25 |
| Thermal Shock Resistance, points | 12 to 15 | |
| 22 |