Austenitic Nodular Cast Iron vs. C70400 Copper-nickel
Austenitic nodular cast iron belongs to the iron alloys classification, while C70400 copper-nickel belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is austenitic nodular cast iron and the bottom bar is C70400 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 to 190 | |
| 120 |
| Poisson's Ratio | 0.29 to 0.3 | |
| 0.34 |
| Shear Modulus, GPa | 70 to 72 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 500 | |
| 300 to 310 |
| Tensile Strength: Yield (Proof), MPa | 190 to 240 | |
| 95 to 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 to 350 | |
| 210 |
| Melting Completion (Liquidus), °C | 1340 to 1400 | |
| 1120 |
| Melting Onset (Solidus), °C | 1300 to 1360 | |
| 1060 |
| Specific Heat Capacity, J/kg-K | 470 to 490 | |
| 390 |
| Thermal Expansion, µm/m-K | 13 to 14 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 to 25 | |
| 32 |
| Density, g/cm3 | 7.7 to 8.0 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.5 to 4.9 | |
| 3.0 |
| Embodied Energy, MJ/kg | 48 to 68 | |
| 47 |
| Embodied Water, L/kg | 91 to 120 | |
| 300 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 98 to 160 | |
| 38 to 220 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 24 to 25 | |
| 19 |
| Strength to Weight: Axial, points | 15 to 18 | |
| 9.3 to 9.8 |
| Strength to Weight: Bending, points | 16 to 18 | |
| 11 to 12 |
| Thermal Shock Resistance, points | 12 to 15 | |
| 10 to 11 |